QFH Hot Cross Hatch Adhesion Tester

Product Introduction

This instrument and is designed and manufactured according to the standard 

of ISO2409-1992. 

Applicable to GB /T9286-98, BS 3900E6/ASTM D3359.

The instrument draw the grid of a certain size by a certain specification of the tools 

by using the uniform force,cut and penetrate the coating to be a grid lattice graphics, 

to evaluate the adhesion of coating on the substrate through the assessment of the

full extent of the grid.

Uses

The instrument is mainly suitable for organic coating adhesion assay Hatch.

Applies not only to the laboratory,the construction site can also be used under

various conditions.

Working principle and scope
The instrument is a certain specification tool that will make the coating lattice graphics 

cut and penetrate,hatch completed by six graphic classification, assess the effect of the

coating adhesion separated from the substrate.

Technical Specification
1.Multi-blade cutter spacing are: 1+0.01mm, 2+0.01mm.
2.Multi-blade cutter addendum straightness were: ¡Û0.003mm¡Û0.006mm.
3.Multi-blade cutter working tooth tip width: ¡Û0.05mm.

Instruction
1.The specimen must be prepared according to ISOR1514  and ISO2828 requirements.

2.The test piece is placed on the tablet hardness sufficient.

3. Handheld Hatch handle, so multi-blade cutter perpendicular to the specimen plane. 

4.With uniform pressure, steady approach does not vibrate and  20-50mm / S cutting 

speed cutting program.

5.The specimen is rotated 90 degrees on the cutting stroke cuts repeat the above operation,

so as to form a lattice graphics.

6.With a soft bristle brush on both sides of the diagonal lattice pattern gently back 5 times,

5 times forward brush specimens.

7.The test at least at three different locations on the test piece is completed,if the test 

results of three different positions, the experiment should be repeated at more than three positions, all while recording the results.

To replace the multi-blade cutter, use a screwdriver blade Loosen the two screws,

put the knives, knife blade attached to the handle side of the site, and tighten the screws.

Please Attention
1.All cuts should be through the coating, but not too deep cut substrates.

2.As a result of the coating is too thick and hard and can not penetrate the

material in the end,the experiment is not valid, but it should be stated in the test report.

3.The test must be a US company 3M tape produced 610-1PK special tape test(or otherwise specified test tape). The tape posted on the whole cross hatch, and then

tore off the minimum angle, the result may be in proportion to the gum off the area 

determined according to the film surface.

4.The test should be carried out at a temperature of 23 ¡À 2 ¡æ and relative humidity

of 50 ¡À 5%.

Adhesion Test Class:

ISO Class

¡¡

ASTM Class

¡¡

Test Results

¡¡

Peeling area ratio

             S

0 5B

The incision edges are smooth,

without any peeling

S=0%

¡¡

1 4B

The incision at the crossing

 of minor peeling

0£¼S¡Ü5%

¡¡

2 3B

The incision edges and the crossing

of a small piece of peeling

5%£¼S¡Ü15%

¡¡

3 2B

The incision edge and the crossing 

of a piece of peeling

15%£¼S¡Ü35%

¡¡

4 1B

The incision edge and the crossing

of large piece of peeling

35%£¼S¡Ü65%

¡¡

5 0B

The incision edge and the crossing 

of a large piece of major peeling

65%£¼S

¡¡

Product Display

What in Package:

1 x Handle
1 x Brush
3 x Blades( 1 x 1mm 11 teeth£¬1 x 2mm 11 teeth£¬1¡Á3mm 6 teeth)
1 x Cross Hatch Cutter
1 x Magnifier
1 x Carry Box
1 x1 roll of 3M Transparent Tape

¡¡

Item Included

QFH Hot Cross Hatch Adhesion Tester(220113)

Item Number Description QTY Unit Note
220113 QFH Hot Cross Hatch Adhesion Tester 1 set ¡¡